Low-heating Portland Cement for volume concrete (HBC)

  • Low-heating Portland Cement for volume concrete (HBC)
  • Low-heating Portland Cement for volume concrete (HBC)
  • Low-heating Portland Cement for volume concrete (HBC)
  • Low-heating Portland Cement for volume concrete (HBC)
  • Low-heating Portland Cement for volume concrete (HBC)
Model No.︰42.5
Brand Name︰CHNGN
Country of Origin︰China
Unit Price︰-
Minimum Order︰-
Share on:

 Total 28 Related Items 
Prev1617181920Next

Product Description
Shenzhen Chenggong Building Materials Co., Ltd. (www.chngn.com) supplying Low-heating Portland Cement.

Low-heating Portland Cement, is also named High Belite Cement (HBC), a kind of high-performance environmentally-friendly energy-saving cement. 

Character: 
1. Low heat of hydration;
2. Lower requirement of water;
3. High durability;
4. Higher rate of development of late strength;
5. More high strength of concrete
6. Lower adiabatic temperature rise will decrease temperature control steps and lower risks of concrete and products rupture;
7. Super-high corrosion resistance, special to sulfate;
8. Excellent dry shrinkage resistance;
9. Good wear resistant, flush resistant;
10. Good stability of volume.

Application:
1. mass concrete
2. hydraulic engineering concrete
3. marine concrete such as seaport, sea wall, dock, road near sea, bridge on sea, marine structure
4. sulfate resistance concrete
5. high-strength concrete
6. anti-crack concrete 
7. steel tube for sulfate resistance
8. Cement products such as cement wall, board, pipe, bricks 
9. floor and road of chemical plant etc,
10. other concrete construction and concrete products.

Packing: 50kg bag and / or big bag




specifications︰1. SO3 3.5%Max
2. MgO 5.0%Max
3. Alkali Content 0.60%Max
4. LOI 3.0%Max
5. Specific Surface: 250m2/kg
6. Initial Setting 60 minutes Min
7. Final Setting 12 hours Max
8. Compressive Strength 13.0MPa Min(7d), 42.5MPa Min(28d)
9. Flexural Strength 3.5MPa Min(7d), 6.5MPa Min(28d)
10. Hydration Heat 230KJ/KG Max(3d), 260KJ/KG Max(7d)
Advantages︰1. Low heat of hydration;
2. Lower requirement of water;
3. High durability;
4. Higher rate of development of late strength;
5. More high strength of concrete
6. Lower adiabatic temperature rise will decrease temperature control steps and lower risks of concrete and products rupture;
7. Super-high corrosion resistance, special to sulfate;
8. Excellent dry shrinkage resistance;
9. Good wear resistant, flush resistant;
10. Good stability of volume.
Export Markets︰worldwide
Pricing︰FOB, CFR, CIF
Payment Details︰T/T, L/C at sight
Min Order︰one 20'FCL
Standard Met︰China GB200-2003
Product Image






Related Products
High Belite Cement (HBC) for volume concrete
High Belite Cement (HBC) for volume concrete
Rapid-demould High-strength Cement for GRC
Rapid-demould High-strength Cement for GRC
Sulfate Resistant Portland Cement(SRC)
Sulfate Resistant Portland Cement(SRC)
type RHC-1 Rapid-hardening Cement for fast stripping product in 15-30 minutes
type RHC-1 Rapid-hardening Cement for fast stripping product in 15-30 minutes

Home  |  Product Catalog  |  Contact Us  |  Sitemap  |  Mobile Version
  English     简体版     繁體版
Powered by DIYTrade.com